317LMN is an austenitic, higher-molybdenum bearing stainless steel further alloyed with nitrogen that is particularly effective in enhancing resistance to pitting and crevice corrosion and also has excellent resistance to chemical attack. Its low carbon composition provides resistance to sensitization during welding and the additional nitrogen serves to increase its strength.
317LMN has the highest aqueous corrosion resistance of all standard stainless steels and also has higher creep, stress-to-rupture, and tensile strength at higher temperatures.
The nitrogen content of 317LMN acts as a strengthening agent giving it a higher yield strength than 317L. 317LMN is also a low carbon grade which enables it to be used in the as-welded condition free from chromium carbide precipitation on the grain boundaries.
Stainless Steel 317LMN Applications
Weight % (all values are maxim1720um unless a range is otherwise indicated)
| Cr | 17-20 | Mn | 2.0 max |
| Ni | 13.5-17.5 | P | 0.045 max |
| Mo | 4.0-5.0 | S | 0.03 max |
| N | 0.1-0.2 | Si | 0.75 max |
| C | 0.03 max | Fe | Balance |
Stainless Steel 317LMN Mechanical Properties
Typical Values at 68°F (20°C)
| Yield Strength | Ultimate Tensile Strength | Elongation | Hardness | ||
| Psi(min) | MPa | Psi(min) | MPa | % (min) | (max) |
| 35,000 | 205 | 80,000 | 550 | 40 | 96 (HRB) |
The properties of 317LMN is similar to other conventional austenitic stainless steels, and can therefore be fabricated in a manner similar to alloys 304 and 306. The alloy is machined using heavy feeds and slow speeds and welded using all common methods. The material is initially forged at temperatures ranging from 1150 to 1205°C (2100-2200°F). It is then annealed at 1080 to1175°C (1975 to 2150°F) followed by air cooling or water quenching. The alloy can be hardened only by cold working.
Available Sizes And Specifications
| 317LMN stainless steel pipe sizes and specifications | |
| Grade | 317LMN |
| Stainless steel seamless pipe | Outside diameter: 4.0 - 1219mm, Thickness: 0.5 -100mm,Length: 24000mm |
| Stainless steel welded pipe | Outside diameter: 6.0 - 2800mm, Thickness: 0.3 -45mm,Length: 18000mm |
| Stainless steel capillary pipe | Outside diameter: 0.4 - 16.0mm, Thickness: 0.1 -2.0mm,Length: 18000mm |
| Stainless steel welded sanitary pipe | Outside diameter:8.0- 850mm, Thickness: 1.0 -6.0mm |
| Stainless steel seamless sanitary pipe | Outside diameter: 6.0- 219mm, Thickness: 1.0 -6.0mm |
| Stainless steel square pipe | Side Length: 4*4 - 300*300mm, Thickness: 0.25 - 8.0mm, Length: 18000mm |
| Stainless steel rectangular pipe | Side Length: 4*6 - 200*400mm, Thickness: 0.25 - 8.0mm, Length: 18000mm |
| Stainless steel coil pipe | Outside diameter: 0.4 - 16mm, Thickness: 0.1 - 2.11mm |
| Standard | American Standard: ASTM A312, ASME SA269, ASTM A269, ASME SA213, ASTM A213 ASTM A511 ASTM A789, ASTM A790, ASTM A376, ASME SA335, B161, SB163, SB338, SB667/668Germany Standard: DIN2462.1-1981, DIN17456-85, DIN17458-85·European Standard: EN10216-5, EN10216-2Japanese Standard: JIS G3463-2006, JISG3459-2012Russian Standard: GOST 9941-81 |
Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .
Q2: Can I have free sample before making orders?
){kind=link}