| Customization: | Available |
|---|---|
| Product Type: | Rod |
| Material: | Iron-Nickel-Cobalt Alloy |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
LORK is a alloy manufacturer with 20 years of manufacturing experience.
WASPALOY is a nickel based age hardenable alloy that possesses high temperature strength while still having a good corrosion resistance, especially to oxidation. WASPALOY can be used at temperatures up to 650°C (1200°F) which is critical rotating applications. WASPALOY is used in gas turbine engine components, missile systems, shafts, spacers, seals, rings, casings, fasteners and many other uses in engine hardware, airframe assemblies.
Waspaloy 25 is a nickel- base alloy with excellent high-temperature strength and good resistance to oxidation at a temperature up to 1800° F. This superalloy has higher stability and strength ranges than those available for alloy 718. Waspaloy 25™ can be heat treated through a three-step process: solution treatment, stabilization, and age-hardening.
Nickel Cobalt Alloy Waspaloy 25 Applications
Properties as per AMS 5708 type 2 (capable of AMS 5709) Heat Treatment is as follows
Solution Treat 1900 - 1975°F / 1-4 hours and Air Cool
Resulting hardness not higher than 302HB
Stabilization Heat Treatment Heat to 1550°F / 4 hrs and Air Cool
Precipitation Heat Treatment Heat to 1400°F / 16 hrs and Air Cool
Resulting hardness 32-42 HRC
Heat Treatment is as follows
Annealing 1975°F / 30 mins and Air Cool
Solution Heat Treatment 1825°F / 2hrs and Air Cool
Stabilization Heat Treatment 1550°F /4hrs and Air Cool
Precipitation Heat Treatment 1400°F / 16 hrs and Air Cool
Nickel Alloy Waspaloy 25 Specifications
1.Rod, Bar, Wire and Forging Stock
2.ASTM B 637, ISO 9723, ISO 9724, ISO 9725, AMS 5704, AMS 5706, AMS 5707, AMS 5708, AMS 5709, AMS 5828, MAM 5706, AECMA PrEN 2193, AECMA PrEN 2194, AECMA PrEN 2406, AECMA PrEN 2958, AECMA PrEN 2959, AECMA PrEN 2960, AECMA PrEN 3220.
3.Plate, Sheet and Strip
4.AMS 5544, AECMA PrEN 2195
5.Other
6.UNS N07001, W. Nr 2.4654, MSRR 7192
| Cr | 18.0-21.0 | B | 0.003-0.01 |
| Zr | 0.02-0.12 | Al | 1.2-1.6 |
| Ti | 2.75-3.25 | Mo | 3.5-5.0 |
| Co | 12.0-15.0 | Cu | 0.5 max |
| Fe | 2.0 max | S | 0.03 max |
| Si | 0.75 max | Mn | 1.0 max |
| C | 0.02-0.1 max | P | 0.03 max |
| Ni | Balance |
| Material | Condition | Thickness | Temp. | Tensile Strength ksi | Yield Strength ksi | Elongation in 4D | Hardness HRC |
| Sheet | Sol Treated, Stabilization + Precipitation HT | 0-0.020" | Room | 170 | 110 | 15 | 34-44 |
| Sheet | Sol Treated, Stabilization + Precipitation HT | 0-0.020" | 1000°F | 145 | 100 | 13 | |
| Sheet | Sol Treated, Stabilization + Precipitation HT | over 0.020" | Room | 175 | 115 | 20 | 34-44 |
| Sheet | Sol Treated, Stabilization + Precipitation HT | over 0.020" | 1000°F | 150 | 105 | 15 |
Waspaloy offers the following key features:
Very high strength at elevated temperatures.
Strength is generally comparable to that of Rene 41 and generally superior to Inconel 718.
Age hardenable.
High temperature dynamic applications.