AM 350 is a chromium-nickel-molybdenum stainless steel which can be hardened by martensitic transformation and/or precipitation hardening. It offers superior corrosion resistance to other quench-hardenable martensitic stainless steels with good high temperature strength. Depending upon the heat treatment, AM 350 may have an austenitic structure for best formability, or a martensitic structure with strengths comparable to those of martensitic steels. The alloy normally contains about 5 to 10% delta ferrite and its corrosion resistance of approaches that of the chromium-nickel austenitic stainless steels.
The table below provides the compositional ranges of grade AM350 stainless steels:
Composition ranges of grade AM350 stainless steels
|
|
|
|
|
|
|
|
|
|
|
|
904L |
max. |
0.11 |
1.25 |
0.05 |
0.040 |
0.035 |
|
3.25 |
5.0 |
| Grade | UNS | DIN | EN | AMS | ASTM | JIS | |
AM350 |
S35000 |
- |
AMS 5548 |
ASTM A693 |
- | ||
Ultimate Tensile Strength: 200 KSI max (1380 MPa max)
Yield Strength: (0.2% offset) 85 KSI max (585 MPa max)
Elongation:
8% min: gauges < 0.010 inches
12% min: gauges > 0.010 inches
Hardness: Re 30 max
Typical 850°F
Ultimate Tensile Strength: 185 KSI min (1275 MPa min)
Yield Strength: (0.2% offset) 145 KSI min (1000 MPa min)
Elongation:
2% min: gauges 0.0005 - 0.0015 inches
4% min: > 0.0015 - 0.002 inches
6% min: > 0.002 - 0.010 inches
8% min: > 0.010 inches
Typical 1000°F
Ultimate Tensile Strength: 165 KSI min (1140 MPa min)
Yield Strength: (0.2% offset) 150 KSI min (1035 MPa min)
Elongation:
2% min: auges 0.0005 - 0.0015 inches
4% min:> 0.0015 - 0.002 inches
6% min: > 0.002 - 0.010 inches
8% min: > 0.010 inches
Bellows
Industrial cutters and knives
Gas turbine components