Lork Group specializes in the supply of 8AI-1Mo-1V alloy raw materials and processing, alloys, stainless steel, metal quality development, welcome your inquiries
Titanium 8-1-1 is a near alpha alloy with aluminum being the alpha stabilizer and the additions of Mo, V, and Fe, which result in a small amount of beta formation. Ti 8-1-1 can provide creep resistance at operating temperatures up to 450°C (842°F). Ti 8-1-1 has the highest modulus and lowest density of all Ti alloys. It is notable not only for its high strength and creep resistance but also for a good stiffness-to-density ratio and toughness. It is typically used (but is not limited to) a variety of jet engine applications such as forged compressor blades and discs.
Titanium 8-1-1 may be either hot or cold-formed. Popular methods include hydro-press, stretch or drop-hammer. It responds similarly to 300 series stainless steel. Hot forming will reduce both the spring-back and required forming forces of Ti 8-1-1 and will increase its overall ductility. The cold working characteristics of Ti 8-1-1 are similar to those of austenitic stainless steel. In multiple forming operations, intermediate stress relieving is recommended to offset Ti 8-1-1's tendency to work harden. Post-work annealing is required to regain optimal performance characteristics.
Titanium 6AL-6V-2SN Alloy Application Industries
6AL-6V-2SN Titanium Alloy Chemical Composition
The chemical composition of 6AL-6V-2SN alloy is outlined in the following table.
| Element | Content (%) |
| Titanium, Ti | 82.895 - 87.8 |
| Aluminum, Al | 6.0 |
| Vanadium, V | 6.0 |
| Tin, Sn | 2.0 |
| Carbon, C | ≤0.050 |
| Copper, Cu | 0.35 - 1.0 |
| Hydrogen, H | ≤0.015 |
| Iron, Fe | 0.35-1.0 |
| Nitrogen, N | ≤0.040 |
| Oxygen, O | ≤0.20 |
| Properties | Metric | Imperial |
| Hardness, Brinell | 351 | 351 |
| Hardness, Knoop | 382 | 382 |
| Hardness, Rockwell C | 38 | 38 |
| Hardness, Vickers | 367 | 367 |
| Tensile Strength, Ultimate | 1050 MPa | 152000 psi |
| Elongation at Break | 14% | 14% |
| Poissons Ratio | 0.32 | 0.32 |
The physical properties of 6AL-6V-2SN alloy are tabulated below.
| Properties | Metric | Imperial |
| Density | 4.54 g/cc | 0.164 lbs/in3 |
| Melting Point | 1627-1649°C | 2961-3000°F |
| Specific Heat Capacity | 0.670 J/g-°C | 0.160 BTU/lb-°F |
| Modulus of Elasticity | 110.3 GPa | 16000 ksi |
| Thermal Conductivity | 6.60 W/m-K | 45.8 BTU-in/hr-ft²-°F |