LORK is a special stainless steel manufacturer with 20 years of manufacturing experience.
305 Stainless Steel is an austenitic chromium nickel stainless steel with a low rate of work hardening. This low rate of work hardening makes it suitable for many deep drawing applications. In order to minimize earring during drawing, the directionality introduced during cold rolling must be kept to a minimum amount. Deep drawing quality should be noted when ordering this alloy. Ordering annealed or dead soft does not guarantee deep drawing quality. Type 305 is non magnetic and becomes magnetic ( at a slow rate) with increasing cold work.
Stainless Steel 305 Applications
Grade 305 stainless steel can be welded using most of the resistance and fusion methods. Oxyacetylene welding is not preferred for this steel.
Hot working of grade 305 stainless steel can be done at 1149 to 1260°C (2100 to 2300°F). This process is followed by rapid cooling to obtain maximum corrosion resistance.
Grade 305 stainless steel can be drawn, spun, headed and blanked due to its low work hardening rate.
Grade 305 stainless steel can be annealed at temperature ranging from 1010 to 1121°C (1850 to 2050°F) followed by rapid cooling.
Grade 305 stainless steel is unresponsive to heat treatment. The hardness and strength of the steel can be increased through cold working.
The following table shows the chemical composition of grade 305 stainless steel.
| Element | Content (%) |
| Iron, Fe | 67 |
| Chromium, Cr | 18 |
| Nickel, Ni | 12 |
| Manganese, Mn | ≤ 2 |
| Silicon, Si | ≤ 1 |
| Carbon, C | 0.12 |
| Phosphorous, P | 0.045 |
| Sulfur, S | 0.030 |
The following table shows the chemical composition of grade 305 stainless steel.
| Element | Content (%) |
| Iron, Fe | 67 |
| Chromium, Cr | 18 |
| Nickel, Ni | 12 |
| Manganese, Mn | ≤ 2 |
| Silicon, Si | ≤ 1 |
| Carbon, C | 0.12 |
| Phosphorous, P | 0.045 |
| Sulfur, S | 0.030 |
Other designations that are equivalent to grade 305 stainless steel include the following.
| AMS 5514 | ASTM A240 | ASTM A478 | QQ S766 |
| AMS 5686 | ASTM A249 | ASTM A492 | DIN 1.4303 |
| ASME SA193 | ASTM A276 | ASTM A493 | UNI X 8 CrNi 19 10 |
| ASME SA194 | ASTM A313 | ASTM A511 | JIS SUS 305 |
| ASME SA240 | ASTM A314 | ASTM A554 | JIS SUS 305 J1 |
| ASTM A167 | ASTM A320 (B8P, B8PA) | ASTM A580 | SAE 30305 |
| ASTM A193 (B8P, B8PA) | ASTM A368 | DIN 1.4303 | SAE J405 (30305) |
| ASTM A194 (8P, 8PA) | ASTM A473 | QQ S763 |
| 305 stainless steel plate sizes and specifications | |
| Grade | 305 |
| Cold rolled stainless steel plate | Thickness: 0.3mm- 16.0mm, Width: 1000mm - 2000mm,Length: as requirements, Surface: 2B/BA/SB/8K/HL/1D/2D etc |
| Hot rolled stainless steel sheet | Thickness: 3.0mm - 300mm, Width: 1000mm - 3000mmLength: as requirements, Surface: No.1/pickling |
| Standard | ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303,BS 1449, DN17441, G4305 |
| Stainless steel plate | Thickness: 8.0mm - 300mm, Width: 1000mm - 3000mmLength: as requirements, Surface: No.1/pickling |
Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .
Q2: Can I have free sample before making orders?
){kind=link}