Wholesale Private Label R30035/ASTM F562/2.4999 Medical Materials Alloy Sheet for Dental Equipment MP35n Dental Material Cobalt-Based Alloy Plate

• Customization: Available
• Surface Treatment: Polishing
• Shape: Sheet
• Model NO.: MP35N Sheet/Plate
• Color: Bronze
• Material: Nickel
• Key Words: MP35n Plate/Sheet
• Thickness: 2mm - 100mm
• Length: as Your Requirments
• Diameter Tolerance: H9, H11, H13, K9, K11, K13 etc
• Sample: Free-Sample
• Surface: Lack, Peeled, Polishing, Bright, Sand Blast, Hl
• MOQ: 100kgs
• Stock: in Stock
• Transport Package: Wooden Package
• Specification: MP35N
• Trademark: LORK
• Origin: China
• HS Code: 7219350000
• Production Capacity: 50000kg/Month

Product Description

Product Description

Introduction

MP35N is an age hardenable Nickel-Cobalt base alloy that has a unique combination of properties - ultra high strength, toughness, ductility and outstanding corrosion resistance. MP35N resists corrosion in hydrogen sulphide, salt water and other chloride solutions. It also has excellent resistance to crevice and stress corrosion cracking in sea water and other hostile environments.

The four alloy elements in MP35N are the basis for corrosion resistance in almost every Stainless Steel, Nickel and Cobalt-based alloy commonly used in the industry. The alloy resists corrosion in hydrogen sulphide, salt water and other Chloride solutions, as well as the mineral acids (Nitric, Hydrochloric and Sulphuric).

MP35N is suitable where a high combination of strength, high modulus values and good corrosion resistance are required.

Applications for this alloy also include medical devices and dental products.

Composition

 

The chemical composition of MP35N is indicated in the table below:

Element	Min %	Max %
C	-	0.025
P	-	0.015
Si	-	0.15
Ni	33.00	37.00
Co	bal
Mn	-	0.15
S	-	0.01
Cr	19.00	21.00
Mo	9.00	10.50
Ti	-	1.00
Fe	-	1.00

Grade Specification

Grade	UNS	DIN	EN	AMS	ASTM	JIS
MP35N	R30035		2.4999	AMS 5844 AMS 5845	ASTM F562

Mechanical Properties

Material	Condtion	Ultimate Tensile Strength ksi	0.2 % Yield Strength ksi	Elongation %	Reduction of Area %	Hardness HRC
MP35N  AMS 5844	Solution Heat Treated and Work Strengthened	255	225	12	50	45
MP35N AMS 5845	Solution Heat Treated and Work Strengthened and Aged	260	230	8	35	38 min

 

 

Characteristic

Combination of high strength, ductility and good mechanical properties at ambient temperatures.
Excellent corrosion resistance in hydrogen sulphide.
Excellent resistance to crevice and stress corrosion cracking in sea water.
Age hardenable (Spring Temper only).
Outstanding corrosion resistance
High strength & ductility
Good mechanical properties at ambient temperatures
Excellent resistance to crevice & stress corrosion cracking
Meets UNS R30035 specifications


Heat Treatment (Aging)

MP35N should be aged at the temperature required to achieve the final properties desired. The amount of cold work in MP35N defines the recommended aging treatments. For AMS 5844 (fully strength/heavily cold worked) material, the alloy should be ages at 1000ºF - 1200ºF for 4 hours. For optimum sulphide SCC resistance, less-heavily cold worked material can be aged at 1300ºF or 1350ºF for 4 hours or at 1425ºF for 6 hours as indicated in NACE MR-0175. The 425ºF aging treatment provides the best sulphide SCC resistance, but at the expense of strength. Exposure to temperatures much above the recommended aging temperatures may result in significant (and nonrecoverable) loss in strength cause by the reversion of the cold-worked metallurgical structure to the much softer annealed structure.


Applications

Aerospace fasteners
Tie rods
Chemical processing
Medical devices
Dental equipment
Cryogenic equipment
Marine equipment
Oil & gas
Food processing
 

 

Surface Treatment

 

 

 

Processing

 

Packaging & Shipping