LORK exports a wide range of Aluminium 2014 tube which performs brilliantly in large temperature and concentration ranges.
This alloy ranks among the strongest heat treatable products available. It combines excellent strength with good machinability. Aluminum 2014 is one of the easiest aluminum alloys to weld and it performs well with arc and resistance welding methods. However, its corrosion resistance is limited. When exposure to the elements is anticipated, alloy 2014 should be clad with pure aluminum or painted for protection. Alloy 2014 is an excellent forging alloy for aircraft parts such as landing gears and hydraulic cylinders.
5083 Aluminum Alloy Applications
• Ship Building
• Rail Cars
• Vehicle Bodies
• Tip Truck Bodies
• Mine Skips and Cages
• Pressure Vessels
The following table shows the chemical composition of Aluminium / Aluminum 5083 alloy.
| Element | Content (%) |
| Aluminum, Al | 92.4 - 95.6 |
| Magnesium, Mg | 4.0 - 4.9 |
| Mangnese, Mn | ≤ 1.0 |
| Silicon, Si | ≤ 0.40 |
| Iron, Fe | ≤ 0.40 |
| Chromium, Cr | ≤ 0.25 |
| Zinc, Z | ≤ 0.25 |
| Titanium, Ti | ≤ 0.15 |
The physical properties of Aluminium / Aluminum 5083 alloy are tabulated below.
| Properties | Metric | Imperial |
| Density | 2650 kg/m³ | 0.0961 lb/in³ |
| Melting Point | 591-638°C | 1095-1180°F |
The mechanical properties of Aluminium / Aluminum 5083 alloy are outlined in the following table.
| Properties | Metric | Imperial |
| Hardness, Brinell | 77 | 77 |
| Hardness, Knoop | 100 | 100 |
| Hardness, Vickers | 87 | 87 |
| Ultimate Tensile Strength | 290 MPa | 42000 psi |
| Tensile Yield Strength | 145 MPa | 21000 psi |
| Elongation at Break | 22% | 22% |
| Modulus of Elasticity | 70.3 GPa | 10200 ksi |
| Compressive Modulus | 71.7 GPa | 10400 ksi |
| Notched Tensile Strength | 269 MPa | 39000 psi |
| Ultimate Bearing Strength | 552 MPa | 80100 psi |
| Bearing Yield Strength | 248 MPa | 36000 psi |
| Poisson's Ratio | 0.33 | 0.33 |
| Fatigue Strength | 150 MPa | 21800 psi |
| Machinability | 30% | 30% |
| Shear Modulus | 26.4 GPa | 3830 ksi |
| Shear Strength | 172 MPa | 25000 psi |
The thermal properties of Aluminium / Aluminum 5083 alloy are given in the following table.
| Properties | Metric | Imperial |
| CTE, linear 68°F | 23.8 µm/m-°C | 13.2 µin/in-°F |
| CTE, linear 250°C | 26 µm/m-°C | 14.4 µin/in-°F |
| Specific Heat Capacity | 0.9 J/g-°C | 0.215 BTU/lb-°F |
| Thermal Conductivity | 117 W/m-K | 810 BTU-in/hr-ft²-°F |
| Solidus | 591 °C | 1095 °F |
| Liquidus | 638 °C | 1180 °F |
Other designations that are equivalent to Aluminium / Aluminum 5083 alloy include: