| Customization: | Available |
|---|---|
| Product Type: | Rod |
| Material: | Cobalt-Based Alloy Alloy |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
LORK is a alloy manufacturer with 20 years of manufacturing experience.
Udimet 720 Chemical Composition
| Element | Content (%) |
| Nickel, Ni | 55.16-59.705 |
| Chromium, Cr | 15.5-16.5 |
| Cobalt, Co | 14.0-15.5 |
| Titanium, Ti | 4.75-5.25 |
| Molybdenum, Mo | 2.75-3.25 |
| Aluminum, Al | 2.25-2.75 |
| Tungsten, W | 1.00-1.50 |
| Zirconium, Zr | 0.0250-0.0500 |
| Boron, B | 0.0100-0.0200 |
| Carbon, C | 0.0100-0.0200 |
Udimet 720 Mechanical Properties
| Heat treatment |
RP0,2
(N/mm2) |
Rm
(N/mm2) |
A5
(%) |
Hardness
HRc / HV |
| AW | >9860 | >20 |
Fabrication and Heat Treatment
Annealing
Udimet 720 is annealed at 1121°C (2050°F) and then cooled in air in a rapid manner.
Standard tooling methods are used for cold working Udimet 720. Usage of plain carbon steels is not recommended as they may produce galling. Galling can be reduced by the usage of soft die materials and heavy duty lubricants. Tooling is recommended in the cold working process to allow liberal radii and clearances.
Welding processes recommended for Udimet 720 include gas-tungsten arc welding, gas metal-arc welding and shielded metal-arc welding. Submerged-arc welding is not recommended as cracks may develop due to the high heat input. This alloy can be welded by the commonly used welding procedures and the welding surfaces should be free from paint, crayon markings or oil.
Udimet 720 is capable of being forged as it is ductile.
Conventional methods are used to readily form Udimet 720 that has good ductility. To obtain good forming results a powerful equipment is used along with heavy-duty lubricants. Usage of heavy-duty lubricants is recommended during the cold forming process of this alloy. After the forming process all traces of the lubricant should be cleaned to prevent embrittlement of this alloy at high temperatures.
Udimet 720 can be machined by conventional machining methods and contains higher strength, gumminess and work-hardening qualities. Work-hardening of the alloy before the cutting process and chatter can be minimized by tooling and a heavy duty machining equipment. Usage of water-base coolants is preferred for milling, turning or grinding. Usage of heavy lubricants is preferred for boring, drilling, broaching or tapping operations.
Udimet 720 is treated under four different temperatures to be air-hardened.
Udimet 720 can be age-hardened in the heat-treatment process.