| Customization: | Available |
|---|---|
| Type: | Steel Plate |
| Standard: | ASTM, AISI, GB, JIS, DIN, BS |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
This low carbon austenitic stainless steel is initially electric-arc melted and is then Vacuum Arc Remelted (VAR). This refinement to the purity and homogeneity of the metal produces an high reliability product.
| Element | Min % | Max % |
| Iron (Fe) | Balance | Balance |
| Manganese (Mn) | 2.00 | 2.00 |
| Chromium (Cr) | 18.0 | 20.0 |
| Silicon (Si) | 0.75 | 0.75 |
| Nickel (Ni) | 8.00 | 12.0 |
| Sulfur (S) | 0.03 | 0.03 |
| Carbon (C) | 0.03 | 0.03 |
| Nitrogen (N) | 0.10 | 0.10 |
| Phosphorus (P) | 0.00 | 0.04 |
| Properties | Metric | English |
| Tensile Strength | 483 MPa | 70,000 PSI |
| Yield Strength | 173 MPa | 25,000 PSI |
| Elongation (at break) | 40% | 40% |
| Hardness (Rockwell B) | 92 HRB Max. | 92 HRB Max. |
| Metric |
English |
|
|
Density |
7.29 g/cm³ | 0.285 lbs/in³ |
|
Modulus of elasticity |
193 GPa | 28.0 Mpsi |
|
Electrical resistivity |
720 µohms*mm |
28.4 µohms*in |
|
Thermal conductivity |
15.65 W/(m*°C) |
9.05 BTU*in/(hr*ft²*°F) |
|
Coefficient of linear thermal expansion |
16.92 µm/(m*°C) |
9.4 µin/(in*°F) |
| Grade | UNS | DIN | EN | AMS | ASTM | JIS | |
| 304LV |
UNS S30400 |
- |
ASTM A 276 |
||||