| Customization: | Available |
|---|---|
| Product Type: | Rod |
| Material: | Nife |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Super alloys have good oxidation and creep resistance and can be strengthened by precipitation hardening, solid-solution hardening and work hardening methods. They can also function under high mechanical stress and high temperatures and also in places that require high surface stability.
Hastelloy C276 is a wrought corrosion-resistant alloy that resists the development of grain boundary precipitates that degrade corrosion resistance.
The following datasheet provides an overview of Hastelloy C276.
The chemical composition of Hastelloy C276 is outlined in the following table.
| Element | Content (%) |
|---|---|
| Nickel, Ni | 57 |
| Molybdenum, Mo | 15-17 |
| Chromium, Cr | 14.5-16.5 |
| Iron, Fe | 4-7 |
| Tungsten, W | 3-4.50 |
| Cobalt, Co | 2.50 |
| Manganese, Mn | 1 |
| Vanadium, V | 0.35 |
| Silicon, Si | 0.080 |
| Phosphorous, P | 0.025 |
| Carbon, C | 0.010 |
| Sulfur, S | 0.010 |
The following table shows the physical properties of Hastelloy C276.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.89 g/cm³ | 0.321 lb/in³ |
| Melting point | 1371°C | 2500°F |
The mechanical properties of Hastelloy C276 are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (@thickness 4.80-25.4 mm, 538°C/@thickness 0.189-1.00 in, 1000°F) | 601.2 MPa | 87200 psi |
| Yield strength (0.2% offset, @thickness 2.40 mm, 427°C/@thickness 0.0945 in, 801°F) | 204.8 MPa | 29700 psi |
| Elastic modulus (RT) | 205 GPa | 29700 ksi |
| Elongation at break (in 50.8 mm, @thickness 1.60-4.70 mm, 204°C/@thickness 0.0630-0.185 in, 399°F) | 56% | 56% |
| Hardness, Rockwell B (plate) | 87 | 87 |
The thermal properties of Hastelloy C276 are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@24-93°C/75.2-199°F) | 11.2 µm/m°C | 6.22 µin/in°F |
| Thermal conductivity (-168 °C) | 7.20 W/mK | 50.0 BTU in/hr.ft².°F |
Equivalent materials to Hastelloy C276 are as follows.
| ASTM B366 | ASTM B574 | ASTM B622 | ASTM F467 | DIN 2.4819 |
| ASTM B575 | ASTM B626 | ASTM B619 | ASTM F468 | |
Annealing |
Hastelloy C276 is generally used in the solution treated condition. This alloy is soaked at 1121°C (2050°F) and then quenched in a rapid manner. |
Cold Working |
Conventional cold working procedures are used for cold working Hastelloy C276. |
Welding |
Hastelloy C276 is capable of being welded by the commonly used welding methods. During the welding process excessive input of heat should be avoided. For corrosive applications this alloy is capable of being used in the "as-welded" condition without the need for more heat treatment. |
Forging |
Conventional methods are used to forge or hot-upset Hastelloy C276. |
Forming |
Hastelloy C276 can be formed by being cold worked using conventional techniques. |
Machinability |
Hastelloy C276 has good machinability characteristic. |
Heat Treatment |
Hastelloy C276 is solution heat treated at 1121°C (2050°F) and then quenched rapidly. In case of forging or hot forming, the parts should first be solution heat treated before usage. |
Hardening |
Hastelloy C276 is cold worked to be hardened. |