| Customization: | Available |
|---|---|
| Type: | Stainless Steel Sheets |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
LORK is a special stainless steel manufacturer with 20 years of manufacturing experience.
254 SMO is a high end, molybdenum and nitrogen alloyed super austenitic stainless steel with low carbon content. It demonstrates outstanding resistance to pitting, crevice corrosion stress cracking, and corrosion fatigue uniform corrosion. 254 SMO is substantially stronger than the common austenitic grades, with strength nearly twice that of 300 series stainless steel. It is also characterized by high ductility and impact strength. With high levels of chromium, molybdenum, and nitrogen, 254 SMO is frequently used in high chloride environments, such as brackish water, seawater, pulp mill bleach plants, and other chloride process streams. In some applications it has even been found to be a more cost effective substitute for high nickel and titanium alloys.
Duplex Stainless 254 SMo Applications
Due to its high levels of molybdenum and nickel, Alloy 254 SMO is frequently used in high chloride environments. Examples of applications that call for the used of Alloy 254 SMO include:
▪ Petroleum production
▪ Saltwater handling
▪ Food and chemical processing equipment
▪ Pulp mill bleach systems
▪ Flue gas desulphurization scrubbers
▪ Tall oil distillation columns
▪ Offshore oil & gas production equipment
▪ Desalination equipment
|
Weight % |
C |
Si |
Mn |
S |
P |
Cr |
Ni |
Mo |
N |
Cu |
W |
|
Min. |
|
|
|
|
|
24,00 |
6,00 |
3,00 |
0,20 |
0,50 |
0,50 |
|
Max. |
0,030 |
1,00 |
1,00 |
0,010 |
0,030 |
26,00 |
8,00 |
4,00 |
0,30 |
1,00 |
1,00 |
PREN= (Cr%+3.3Mo%+16N%) ≥ 40
Product Standards: EN 10088-3, ASTM A276, ASTM A479, ASTM A182-11A
(Chemical composition and mechanical properties only)
Approvals: NACE MR0175, NORSOK M650, NORSOK M630 MDS D53/ D54/ D55/ D57
|
Yield strength Rp0.2, MPa |
Tensile strength Rm, MPa |
Elongation [%] |
Hardness [HB] |
Impact, Charpy-V, -46ºC [J] |
Pre |
|
|
Bar |
≥ 550 |
≥ 750 |
≥ 25 |
≤ 310 |
≥ 45 |
≥ 40 |
|
Sheet |
≥ 550 |
750 - 1000 |
≥ 25 |
≤ 310 |
≥ 45 |
≥ 40 |
|
Plate |
≥ 550 |
750 - 930 |
≥ 25 |
≤ 310 |
≥ 45 |
≥ 40 |
|
Plate |
≥ 550 |
750 - 930 |
≥ 25 |
≤ 310 |
≥ 45 |
≥ 40 |
Welding of stainless steel grade 254 SMO requires filler material without which it results in poor strength properties. Filler metals such as AWS A5.14 ERNiCrMo-3, and alloy 625 are recommended. Electrodes used in the process, have to match with AWS A5.11 ENiCrMo-12.
Forging, upsetting and other operations relating to this material can be performed at 982 - 1149°C (1800 - 2100°F). It is recommended that temperatures do not exceed this range as it would result in scaling and reduction in the workability of the material. To re-attain maximum corrosion resistant properties, it is advisable to perform post-process annealing.
Stainless steel grade 254 SMO does not respond to heat treatment. Hardening is possible only through cold reduction.
| 254 SMO stainless steel plate sizes and specifications | |
| Grade | 254 SMO |
| Cold rolled stainless steel plate | Thickness: 0.3mm- 100mm, Width: 1000-mm - 2000mm,Surface: 2B/BA/SB/8K/HL/1D/2D etc |
| Hot rolled stainless steel plate | Thickness: 3.0mm - 100mm, Width: 1000-mm - 2000mm, Surface: No.1/pickling |
| Stainless steel foil | Thickness: 0.02mm- 2mm, Width: Less than 600mm, Surface: 2B |
| Standard | ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303, BS 1449, DN17441, G4305 |
Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .
Q2: Can I have free sample before making orders?