| Customization: | Available |
|---|---|
| Type: | Titanium Wire |
| Application: | Industrial, Medical |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Lork Group specializes in the supply of Grade 5 Ti 6Al 4V ELI alloy raw materials and processing, alloys, stainless steel, metal quality development, welcome your inquiries
Ti 6Al-4V offers a combination of high strength, light weight, formability and corrosion resistance which have made it the most commonly used titanium alloy. It is an alpha+beta alloy that is heat treatable to achieve moderate increases in strength and is recommended for use at service temperatures up to approximately 660°F (350°C). Ti 6Al-4V may be considered in any application where a combination of high strength at low to moderate temperatures, light weight and excellent corrosion resistance are required.
Titanium Grade 5 Ti 6Al 4V Alloy Application Industries
Grade 5 Ti 6Al 4V Titanium Alloy Chemical Composition
The chemical composition of grade 5 Ti 6Al 4V ELI alloy is outlined in the following table.
| Element | Content (%) |
| Titanium, Ti | 90.00 |
| Aluminum, Al | 6.00 |
| Vanadium, V | 4.00 |
| Carbon, C | ≤ 0.10 |
| Oxygen, O | ≤ 0.20 |
| Nitrogen, N | ≤ 0.05 |
| Hydrogen, H | ≤ 0.0125 |
| Iron, Fe | ≤ 0.3% |
| Properties | Metric | Imperial |
| Tensile Strength, Ultimate | ≥895 MPa | ≥130000 psi |
| Tensile Strength, Yield | ≥828 MPa | ≥120000 psi |
| Elongation at Break | ≥10% | ≥10% |
| Modulus of Elasticity | 95.0 - 111 GPa | 13800 - 16100 ksi |
| Shear Modulus | 41.0 - 45.0 GPa | 5950 - 6530 ksi |
The physical properties of grade 5 Ti 6Al 4V alloy are tabulated below.
| Properties | Metric | Imperial |
| Density | 4.43 g/cc | 0.16 lbs/in3 |
| Melting Point | 1604-1660°C | 2920-3020°F |
| Shear Modulus | 43988 MPa | 6.38 x 106 psi |
| Modulus of Elasticity | 113763 MPa | 20885 psi |
| Specific Heat | 0.5263 Joules/g°C | 0.126 BTU/lb-°F |
| Mean Coefficient of Thermal Expansion | 8.6 µm/m-°C | 4.78 µin/in-°F |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F |
The thermal properties of grade 5 Ti 6Al 4V alloy are tabulated below.
| Properties | Metric | Imperial |
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 8.60 µm/m°C | 4.78 µin/in°F |
| Thermal conductivity | 6.70 W/mK | 46.5 BTU in/hr.ft².°F |
The most common market for 6AL-4V is aerospace. Lightweight grade 5 titanium is well suited for applications such as compressor blades, discs, and rings for jet engines; airframe components; pressure vessels; rocket engine cases; helicopter rotor hubs and critical forgings requiring high strength-to-weight ratios. Ti-6AL-4V titanium round bar stock is also age hardenable by heat treatment to achieve even higher strengths. This biocompatible material is also well suited for medical implants. Its mechanical and physical properties allow good capacity for titanium to join with bones and other tissue.
Tooling should consist of tungsten carbide designations C1-C4 or cobalt type high speed tools. Generally, machining characteristics are similar to those of austenitic stainless steels. Ti 6AL-4v Grade 5 Titanium bar stock can be machined using slow speeds, high feed rates, rigid tooling, and flooding the workpiece with non-chlorinated cutting fluid.