Alloy 316H (UNS S31609) is a high carbon modification of Alloy 316 developed for use in elevated temperature service. The alloy has higher strength at elevated temperatures and is used for structural and pressure vessel applications at temperatures above 932°F (500°C). The higher carbon content of 316H also delivers higher tensile and yield strength than 316/316L and its austenitic structure provides excellent toughness down to cryogenic temperatures.
The corrosion resistance of Alloy 316H is comparable to Alloy 316/316L and is superior to Alloy 304/304L in moderately corrosive environments. It is often used in process streams containing chlorides or halides. The alloy resists atmospheric corrosion, as well as, moderately oxidizing and reducing environments. It also resists corrosion in polluted marine conditions.
Alloy 316H is non-magnetic in the annealed condition. It cannot be hardened by heat treatment, however the material will harden due to cold working. It can be easily welded and processed by standard shop fabrication practices.
| Grade | UNS | DIN | EN | AMS | ASTM | JIS |
| S30100 |
|
1.4310 | AMS 5901 AMS 5517 AMS 5518 AMS 5902 AMS 5519 |
ASTM A240 ASTM A666 |
SUS 301 |
| UNS NO | Grade | C | Si | Mn | P | S | Cr | Mo | Ni | N |
| S31609 | 316H | 0.04/0.10 | 0.75 | 2.00 | 0.045 | 0.030 | 16.00/18.00 | 2.00/3.00 | 10.00/14.00 | - |
| UNS No | Grade | Proof Stress 0.2% (MPa) |
Tensile Strength (MPa) |
Elongation A5(%) |
Hardness Max | |
| HB | HRB | |||||
| S31609 | 316H | 205 | 515 | 40 | 217 | 95 |
In most instances the corrosion resistance of Alloy 316H will be comparable to Alloy 316/316L and will have superior corrosion resistance to Alloy 304/304L. Process environments that do not attack Alloy 304/304L will not attack this grade. One exception, however, is in highly oxidizing acids such as acid where stainless steels containing molybdenum are less resistant. Alloy 316H performs well in sulfur containing service such as that encountered in the pulp and paper industry. The alloy can be used in high concentrations at temperatures up to 120°F (38°C).
Alloy 316H also has good resistance to pitting in phosphoric and acetic acids. It performs well in boiling 20% phosphoric acid. The alloy can also be used in food and pharmaceutical process industries where it is utilized to handle hot organic and fatty acids where product contamination is a concern.
Alloy 316H performs well in fresh water service even with high levels of chlorides. The alloy has excellent resistance to corrosion in marine environments under atmospheric conditions.
The higher molybdenum content of Alloy 316H assures it will have superior pitting resistance to Alloy 304/304L in applications involving chloride solutions particularly in oxidizing environments.