| Customization: | Available |
|---|---|
| Type: | Stainless Steel Sheets |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
LORK is a special stainless steel manufacturer with 20 years of manufacturing experience.
S17600 stainless steel is a precipitation-hardening stainless steel formulated for primary forming into wrought products. S17600 is the UNS number for this material. Alloy 635 is the common industry name.
The properties of S17600 stainless steel include four common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare S17600 stainless steel to: wrought precipitation-hardening stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
600 Series Stainless 635 Applications
S35000 is typically used in applications below 1000°F where a combination of strength and good corrosion resistance is required.
- Aerospace applications,
- Edge welded bellows applications,
- Precision seals,
- Couplings for semiconductor processing equipment,
- High vacuum systems,
- Industrial cutting machines,
- Cutting tools and various valves and gas turbine compressor components such as blades, disks, rotors and shafts
and similar parts requiring high strength at room and moderate temperatures.
Specification
- AM 350 (Type 633),
- AISI 350,
- Grade 350,
- SUS 633(JIS),
- ATI AM 350,
- CarTech 350 Alloy (Pyromet alloy 350)
- ASTM A693 / ASME SA693
- AMS 5548
- AMS 5745
- UNS35000
Chemical composition(mass fraction)(wt.%) of the A 693 Type 635
| Elements | Min.(≥) | Max.(≤) |
| C | 0.08 | 0.11 |
| Mn | 1.00 | 1.25 |
| Si | 1.00 | 0.50 |
| P | - | 0.04 |
| S | - | 0.03 |
| Cr | 16.00 | 17.50 |
| Ni | 6.00 | 7.50 |
| AI | - | 0.4 |
| Ti | 0.4 | 1.20 |
| YieldRp0.2 (MPa) | TensileRm (MPa) | ImpactKV (J) | ElongationA (%) | Reduction in cross section on fractureZ (%) | As-Heat-Treated Condition | HBW |
| 263 (≥) | 746 (≥) | 12 | 14 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 324 |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 7.7-8.03 | 25 | - |
|---|---|---|---|
| Poisson's Ratio | 0.27-0.30 | 25 | - |
| Elastic Modulus (GPa) | 190-210 | 25 | - |
| Tensile Strength (Mpa) | 1158 | 25 | oil quenched, fine grained, tempered at 425°C |
| Yield Strength (Mpa) | 1034 | ||
| Elongation (%) | 15 | ||
| Reduction in Area (%) | 53 | ||
| Hardness (HB) | 335 | 25 | oil quenched, fine grained, tempered at 425°C |
| Quantity | Value | Unit |
| Thermal expansion | 16 - 17 | e-6/K |
| Thermal conductivity | 16 - 16 | W/m.K |
| Specific heat | 500 - 500 | J/kg.K |
| Melting temperature | 1370 - 1400 | °C |
| Service temperature | 0 - 500 | °C |
| Density | 8000 - 8000 | kg/m3 |
| Resistivity | 0.7 - 0.7 | Ohm.mm2/m |
| 635 Stainless steel profile sizes and specifications | |
| Grade | 635 |
| Specification | EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO |
| Cold rolled stainless steel plate | Thickness: 0.3mm- 16.0mm, Width: 1000mm - 2000mm, Length: as requirements, Surface: 2B/BA/SB/8K/HL/1D/2D etc |
| Hot rolled stainless steel sheet | Thickness: 3.0mm - 300mm, Width: 1000mm - 3000mm Length: as requirements, Surface: No.1/pickling |
| Standard | ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303, BS 1449, DN17441, G4305 |
| Stainless steel plate | Thickness: 8.0mm - 300mm, Width: 1000mm - 3000mm Length: as requirements, Surface: No.1/pickling |
| Tolerance | H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements |