| Customization: | Available |
|---|---|
| Product Type: | Rod |
| Material: | Nife |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
LORK is a super alloy manufacturer with 20 years of manufacturing experience.
HAYNES 282 alloy (UNS N07208) is a, wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and industrial gas turbine engines. It possesses a unique combination of creep strength, thermal stability, weldability, and fabricability not found in currently available commercial alloys. The excellent creep strength in the temperature range of 1200 to 1700°F (649 to 927°C) surpasses that of Waspaloy alloy, and approaches R-41 alloy without sacrificing weldability.
Haynes 282 Application
▪ sheet fabrications
▪ Rings
▪ Cases found in compressor
▪ Combustion and turbine sections
▪ Engines for aircraft
▪ the transition sections and other hot-gas-path components in land-based gas turbines.
#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. #2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA- Bright annealed cold rolled and bright annealed
#CBA- Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled
#2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements.
* Not all finishes are available for all alloys - Consult Sales for applicable finishes.
Haynes 282 Chemical Composition
| Ni | 57.0 min | Cr | 19.5 |
| Co | 10.0 | Mo | 8.5 |
| Ti | 2.1 | Al | 1.5 |
| Fe | 1.5 max | Mn | 0.3 max |
| Ca | 0.06 | B | 0.005 |
| Temperature | Yield Strength 0.2% Offset |
Ultimate Tensile Strength |
Elongation | |||
| °F | °C | ksi | MPa | ksi | MPa | % |
| RT | RT | 101.4 | 699 | 164.2 | 1132 | 30 |
| 1000 | 538 | 91.6 | 632 | 139.3 | 960 | 36 |
| 1200 | 649 | 91.5 | 631 | 145.7 | 1005 | 27 |
| 1300 | 704 | 90.5 | 624 | 136.5 | 941 | 24 |
| 1400 | 760 | 88.7 | 612 | 120.8 | 833 | 22 |
| 1500 | 816 | 82.3 | 567 | 100.3 | 692 | 24 |
| 1600 | 871 | 72.6 | 501 | 80.5 | 555 | 31 |
| 1700 | 927 | 43.9 | 303 | 50.2 | 346 | 37 |
| 1800 | 982 | 18.7 | 129 | 24.5 | 169 | 61 |
| Haynes 282 available sizes and specifications | |
| Grade | Haynes 282 |
| Nickel plate | Thickness: 0.3mm - 150.0mmWidth: 1000mm - 3000mm |
| Nickel strip/ nickel foil | Thickness: 0.02mm - 16.0mm Width: 5mm - 3000mm |
| Nickel coil | Thickness: 0.3mm - 16.0mm Width: 1000mm - 3000mm |
| Nickel pipe | Outside diameter: 6mm - 1219mm Thickness: 0.5mm - 100mm |
| Nickel Capillary Pipe | Outside diameter: 0.5mm - 6.0mm Thickness: 0.05mm - 2.0mm |
| Nickel bar | Diameter: Ф4mm - Ф600mm |
| Nickel wire rod | Diameter:Ф0.01mm - Ф6mm |
Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .
Q2: Can I have free sample before making orders?
){kind=link}