UNS C63000 is a nickel-aluminum-bronze alloy of copper, which has excellent corrosion resistance and hot formability features. The following datasheet will provide more details about copper UNS C63000.
The following table shows the chemical composition of copper UNS C63000.
| Element | Content (%) |
| Copper, Cu | 82 |
| Aluminium, Al | 10 |
| Nickel, Ni | 5 |
| Iron, Fe | 3 |
The physical properties of copper UNS C63000 are outlined in the following table.
| Properties | Metric | Imperial |
| Density | 7.58 g/cm³ | 0.274 lb/in³ |
| Melting point | 1035°C | 1895°F |
The mechanical properties of copper UNS C63000 are tabulated below.
| Properties | Metric | Imperial |
| Tensile strength | 760 MPa | 110000 psi |
| Yield strength | 470 MPa | 68200 psi |
| Elongation at break (in 50 mm, 10% reduction in area) | 10% | 10% |
| Elastic modulus | 117 GPa | 17000 ksi |
| Poisson's ratio | 0.34 | 0.34 |
| Reduction of area (at 316°C/601°F, cold finished) | 9% | 9% |
| Shear modulus | 44.0 GPa | 6380 ksi |
| Fatigue strength (at number of cycles 1.00e+8, reverse bending) | 255 MPa | 37000 psi |
| Hardness, Rockwell B | 94 | 94 |
| Machinability (UNS C36000 (free-cutting brass) = 100) | 30 | 30 |
The thermal properties of copper UNS C63000 are tabulated below.
| Properties | Metric | Imperial |
| Thermal expansion co-efficient (at 20-300°C/68-572°F) | 16.2 µm/m°C | 9 µin/in°F |
| Thermal conductivity (at 20°C/68°F) | 37.7 W/mK | 262 BTU in/hr.ft².°F |
The machinability rate of UNS C63000 is 30.
Brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding, and butt welding are considered as suitable welding processes, whereas processes such as Soldering and oxyacetylene welding are not recommended for UNS C63000 alloy.
UNS C63000 alloy has a hot forgeability rating of 75 with the recommended hot working temperature ranging between 788 and 927°C (1450 and 1700°F).
The hot working capacity of UNS C63000 is good.
UNS C63000 alloy has poor cold working capacity.
The annealing temperature is between and 593 and 704°C (1100 and 1300°F).
Copper UNS C63000 is used for valve and pump components in industrial process streams. It is also used in marine equipment, high strength fasteners and pole line hardware.