Lork Manufacture AMS 5629/Uns S13800 Steel Rod for Aerospace Components pH 13-8 Mo Stainless Steel Bar

Product Description

Product Description

 

Introduction

Lork Group specializes in the supply of PH 13-8 Mo Bar raw materials and processing, alloys, stainless steel, metal quality development, welcome your inquiries.

PH 13-8 Mo is a stainless steel with approximately 13% chromium and 8% nickel content that has good resistance to corrosion in general as well as to stress corrosion cracking. PH 13-8 Mo offers better mechanical properties in demanding environmental conditions in comparison to other materials based on iron. Precise control of the microstructure is achieved through vacuum melting and remelting. Medium to high strength can be achieved through precipitation hardening aging treatments.

Precipitation-Hardening Stainless Steel PH 13-8 Mo | 1.4534 Applications

• Aerospace components
• Injection molding equipment
• Waterjet cutting equipment
• Petrochemical industries
• Nuclear industries

Stainless Steel PH13-8MO Common Trade Names

• PH13-8Mo
• XM-13
• UNS S13800
• DMS 2100 Grade
• HMS 6-1105 REV A AMD 3
• ST0160LB0013 REV E
• ASTM F899-12B
• RMS-150 REV N for sizes 3.625" Max
• SAE 13-8
• ATI 13-8 Supertough Alloy

Stainless Steel PH13-8MO Chemical Composition

 

Chemical composition - limits in %

Fe	Rest
Cr	12,25 - 13,25
Ni	7,50 - 8,50
Mo	2,00 - 2,50
Al	0,90 - 1,35
Mn	max. 0,20
N	max. 0,10
Si	max. 0,10
C	max. 0,05
P	max. 0,01

PH13-8MO Physical constants and thermal properties

Density	7,76 g/cm³
Melting point	1404 °C
Thermal conductivity at 20°C	12,8 W/m · °C
Elongation coefficient at 20-100°C	13 μm/m · °C

PH13-8MO Typical mechanical properties (room temperature)

H950
Yield strength	min. 1413 MPa
Tensile strength	min. 1517 MPa
Elongation	min. 10 %
H1000
Yield strength	min. 1310 MPa
Tensile strength	min. 1413 MPa
Elongation	min. 10 %
H1050
Yield strength	min. 1138 MPa
Tensile strength	min. 1207 MPa
Elongation	min. 12 %

 

Workability

Hot Working
PH 13-8 Mo stainless can be readily forged, hot headed and upset. Material which is hot-worked must be solution treated prior to hardening if the material is to respond properly to hardening.
Forging
Heat uniformly to 2150/2200°F and hold 1 hr at temperature before forging. Do not forge below 1750°F. To obtain optimum grain size and mechanical properties, forging should be cooled in air to 60°F before further processing. Forging must be solution treated prior to hardening.
Cold Working
PH 13-8 Mo stainless can be fabricated by cold working to an extent which is limited by the high initial yield strength.
Cutting
Bars and forging billets should be cold cut by sawing. Abrasive wheel cutting can cause small surface cracks, particularly when cutting annealed stock, and should be avoided.
Machining
PH 13-8 Mo stainless can be machined in both the solution treated and various age-hardened conditions. In Condition A the alloy gives good tool life and surface finish when machined at speeds 20 to 30% lower then those used for Custom 630 (17Cr-4Ni) or 20 to 30% lower than used for Stainless Type 302 and 304. The machinability as age-hardened will improve as the hardening temperature is increased.
Conditon H 1150M provides optimum machinability. Having procures Conditon H 1150M for best machinability, higher mechanical properties can be developed only by solution treating and heat treating at standard hardening temperatures.
Welding
PH 13-8 Mo stainless can be welded using the inert-gas shielded or resistance welding processes. When a filler metal is required, PH 13-8 welding consumables should provide welds with properties similar to those of the base metal. When designing the weld joint, care should be exercised to avoid stress concentrators, such as shrap corners, threads, and partial-penetration welds. When high weld strength is not needed, a standard austenitic stainless filler, such as E/ER308L, should be considered.
Normally, welding in the solution annealed condition has been satisfactory; however, where high welding stresses are anticipated, it may be advantageous to weld in the overaged (H 1150) condition. Usually, preheating is not required to prevent cracking. If welded in the solution treated condition. the alloy can be directly aged to the desired strength level after welding. However, the optimum combination of strength, ductility and corrosion resistance is obtained by solution treating the welded part before aging. If welded in the overage condition, the part must be solution treated before aging.

Available Sizes And Specifications

 

PH13-8MO stainless steel profile sizes and specifications
Grade	PH13-8MO
Specification	EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO
Standard	AMS 5629/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 ASTM-A167  ASTM-A240  ASTM-A480.
Stainless steel round Bar	Diameter: 2mm - 600mm
Stainless steel bright Bar	Diameter: 2mm - 600mm
Stainless steel hex Bar	Dimension: 6mm - 80mm
Stainless steel square bar	Dimension: 3.0 - 180mm
Stainless steel flat bar	Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm
Stainless steel angle bar	as requirements
Length	Normally 6m, or produce as requirements
Surface	Black, Bright. Peeled and Polished, Solution annealed.
Delivery condition	cold drawn, hot rolled, forged, grinding, centerless grinding
Tolerance	H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements

 

Surface Treatment

 

Detection

Processing

 

Packaging & Shipping

Company Profile

FAQ

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .