Lork 65ni 15.8cr 15.2mo Solution Heat Treated Alloy Rod Corrosion and Heat Resistant AMS5711f Nickel Alloy Bar

Product Description

Product Description

 

Introduction

NITRONIC 50 Stainless Steel provides a combination of corrosion resistance and strength not found in any other commercial material available in its price range. This austenitic stainless has corrosion resistance greater than that provided by Types 316 and 316L, plus approximately twice the yield strength at room temperature. In addition, ANTONNITRONIC 50 Stainless has very good mechanical properties at both elevated and sub-zero temperatures. And, unlike many austenitic stainless steels, NITRONIC 50 does not become magnetic when cold worked.

High Performance Alloys can make hot rolled, cold worked, & strain hardened High Performance Stainless Steel (HPSS) bars in house. Ask for our GFM Bulletin for more information about our bar processing capabilities. We have expanded to enhance product availability.

Austenitic Stainless Steel XM-19 Applications

The following are the list of applications of nitronic 50 alloy:

• Fasteners
• Marine hardware
• Boat shafting
• Pumps and valves

Nitronic 50 chemical composition

Nitronic 50 chemical composition
	Ni	Cr	Mo	Mn	C	Si	Fe
Max	13.5	23.5	3.00	6.0	0.06	1.00	Bal
Min	11.5	20.5	1.50	4.0

Nitronic 50 mechanical properties

Properties	Metric	Imperial
Tensile strength at break	≥ 689 MPa	≥ 100000 psi
Yield strength	≥ 379 MPa	≥ 55000 psi
Elongation at break	≥ 35%	≥ 35%

Nitronic 50 specifications

Form	Standard
Metal Type	UNS S20910
Bar	ASTM A193 ASTM A194 ASTM A276 ASTM A479 AMS 5764
Sheet	ASTM A240 AMS 5861
Plate	ASTM A240 AMS 5861
Forging	ASTM A182 ASTM A193 ASTM A 194 ASTM A276 ASTM A479 AMS 5764
Weld Wire	A5.9 ER209
Din	1.4565

Annealing Temperature
NITRONIC 50 Stainless Steel can be supplied annealed at 1950 F to 2050 F (1066 C to 1121 C). For most applications, the 1950 F (1066 C) condition should be selected, as it provides a higher level of mechanical properties along with excellent corrosion resistance. When as-welded material is to be used in strongly corrosive media, the 2050 F (1121 C) condition should be specified in order to minimize the possibility of intergranular attack.

Corrosion Properties
ANTONNITRONIC 50 Stainless Steel provides outstanding corrosion resistance - superior to Types 316, 316L, 317 and 317L in many media. For many applications the 1950 F (1066 C) annealed condition provides adequate corrosion resistance and a higher strength level. In very corrosive media or where material is to be used in the as-welded condition, the 2050 F (1121 C) annealed condition should be specified. High-Strength (HS) NITRONIC 50 bars are useful for applications such as shafting and bolting, but do not quite exhibit the corrosion resistance of the annealed conditions in all environments.

Intergranular Attack
The resistance to intergranular attack is excellent even when sensitized at 1250 F (675 C) for one hour to simulate the heat-affected zone of heavy weldments. Material annealed at 1950 F (1066 C) has very good resistance to intergranular attack for most applications. However, when thick sections are used in the as-welded condition in certain strongly corrosive media, the 2050 F (1121 C) condition gives optimum corrosion resistance.

Stress-Corrosion Cracking Resistance
In common with most stainless steels, under certain conditions, ANTON NITRONIC 50 Stainless Steel may stress-corrosion crack in hot chloride environments. When tested in boiling 420/0 MgCI2 solution, a very accelerated test, NITRONIC 50 Stainless Steel is between types 304 and 316 stainless steels in resistance to cracking. There is little difference in susceptibility to cracking whether in the annealed, high-strength (HS), or cold-drawn conditions.

Sulfide Stress Cracking
Both laboratory tests and field service experience have shown that ANTON NITRONIC 50 stainless has excellent resistance to sulfide stress cracking in air conditions. NITRONIC 50 in both the annealed and high-strength (hot rolled) conditions has been included in the 1996 revision of NACE Standard MR-01 -75′ "Sulfide Stress Cracking Resistant Metallic Material for Oil Field Equipment," at hardness levels up to RC 35 maximum. The resistance to cracking in laboratory tests in synthetic sour-well solution(5% NaCI + ½% acetic acid. saturated with H2S)

 

Available Sizes And Specifications

XM-19 stainless steel profile sizes and specifications
Grade	XM-19
Specification	EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO
Standard	ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 .
Stainless steel round Bar	Diameter: 2mm - 600mm
Stainless steel bright Bar	Diameter: 2mm - 600mm
Stainless steel hex Bar	Dimension: 6mm - 80mm
Stainless steel square bar	Dimension: 3.0 - 180mm
Stainless steel flat bar	Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm
Stainless steel angle bar	as requirements
Length	Normally 6m, or produce as requirements
Surface	Black, Bright. Peeled and Polished, Solution annealed.
Delivery condition	cold drawn, hot rolled, forged, grinding, centerless grinding
Tolerance	H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements

 

 

Surface Treatment

 

Detection

Processing

 

Packaging & Shipping

Company Profile

FAQ

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .