MP35N is an age hardenable Nickel-Cobalt base alloy that has a unique combination of properties - ultra high strength, toughness, ductility and outstanding corrosion resistance. MP35N resists corrosion in hydrogen sulphide, salt water and other chloride solutions. It also has excellent resistance to crevice and stress corrosion cracking in sea water and other hostile environments.
The four alloy elements in MP35N are the basis for corrosion resistance in almost every Stainless Steel, Nickel and Cobalt-based alloy commonly used in the industry. The alloy resists corrosion in hydrogen sulphide, salt water and other Chloride solutions, as well as the mineral acids (Nitric, Hydrochloric and Sulphuric).
MP35N is suitable where a high combination of strength, high modulus values and good corrosion resistance are required.
Applications for this alloy also include medical devices and dental products.
The chemical composition of MP35N is indicated in the table below:
| Element | Min % | Max % |
|---|---|---|
| C | - | 0.025 |
| P | - | 0.015 |
| Si | - | 0.15 |
| Ni | 33.00 | 37.00 |
| Co | bal | |
| Mn | - | 0.15 |
| S | - | 0.01 |
| Cr | 19.00 | 21.00 |
| Mo | 9.00 | 10.50 |
| Ti | - | 1.00 |
| Fe | - | 1.00 |
| Grade | UNS | DIN | EN | AMS | ASTM | JIS |
| MP35N |
R30035 |
|
2.4999 | AMS 5844 AMS 5845 |
ASTM F562 |
| Material | Condtion | Ultimate Tensile Strength ksi | 0.2 % Yield Strength ksi | Elongation % | Reduction of Area % | Hardness HRC |
| MP35N AMS 5844 |
Solution Heat Treated and Work Strengthened | 255 | 225 | 12 | 50 | 45 |
| MP35N AMS 5845 |
Solution Heat Treated and Work Strengthened and Aged | 260 | 230 | 8 | 35 | 38 min |