Lork Custom ASTM B638/B638m Alloy Steel Rod for Gas Turbine Forgings 660 Stainless Steel Bar

• Customization: Available
• Type: Stainless Steel Bars
• Standard: ASTM, AISI, GB, JIS, DIN, EN
• Model NO.: 660 Bar
• Certification: ISO, AISI, ASTM, GB
• Shape: Round
• Technique: Cold Rolled
• Surface Treatment: Pickling
• Key Words: 660 Bar
• Diameter: 2mm - 600mm
• Width: 1.5mm - 250 mm
• Length: as Your Requirments
• Diameter Tolerance: H9, H11, H13, K9, K11, K13 etc
• Sample: Free-Sample
• Surface: Lack, Peeled, Polishing, Bright, Sand Blast, Hl
• MOQ: 100kgs
• Stock: in Stock
• Transport Package: Wooden Package
• Specification: 660 rod
• Trademark: LORK
• Origin: China
• HS Code: 7219350000
• Production Capacity: 50000kg/Month

Product Description

Product Description

 

Introduction

LORK is a special stainless steel manufacturer with 20 years of manufacturing experience.
 

Alloy 660 is a precipitation hardening austenitic stainless steel known for its impressive strength at high temperatures up to 700°C. Also sold under the names, UNS S66286, and A-286 alloy, Alloy 660 gains its strength from a high degree of uniformity. It has an impressive yield strength minimum of 105,000 psi and is commonly used in high temperature fastening and bolting materials.

Stainless Steel 660 Applications

- Gas turbine forgings, 
- Fasteners, 
- Superchargers, 
- Cryogenic equipment, 
- Missile components, 
- Corrosive deep well hardware 
- Jet engines.

Cold working

Super alloy A-286 is capable of being readily cold worked and a solution anneal heat treatment is recommended when this alloy is work hardened due to severe cold forming. This solution anneal heat treatment will thus enable softening of super alloy A-286.
Welding
Welding methods used for stainless steels are also recommended for super alloy A-286. The area to be welded should be clean. Post welding heat treatment or preheating is not recommended for this alloy. Better welding results can be obtained when this alloy is solution annealed.
Forging
Heavy forging and light forging are suitable for super alloy A-286. Heavy forging is carried out between 1010-1204°C (1850-2200°F) and light forging between 871-1010°C (1600-1850°F).
Forming
Conventional forming methods are used to readily hot or cold form super alloy A-286.
Machinability
Conventional machining techniques are used to readily machine super alloy A-286. This machining process involves turning, drilling and milling. In the turning operations, the usage of cemented carbide tools is recommended for high cutting rates.
Aging
Super alloy A-286 is first solution heat treated at 982°C (1800°F) before the aging process. Aging takes place for 16 h at 718°C (1325°F) after which this alloy is cooled in air.
Hardening
Super alloy A-286 is hardened by the cold working process and is also capable of being age hardened due to the presence of titanium in this alloy.
Heat Treatment
Super alloy A-286 is solution annealed at 982°C (1800°F), oil quenched, held for 16 h at 718°C (1325°F) and finally cooled in air. This heat treatment improves the strength of super alloy A-286.



Stainless Steel 660 Chemical Composition

 

Element	Content (%)
Iron, Fe	54
Nickel, Ni	25.5
Chromium, Cr	14.8
Titanium, Ti	2.13
Molybdenum, Mo	1.30
Manganese, Mn	1.0
Silicon, Si	0.50
Vanadium, V	0.30
Aluminum, Al	0.18
Carbon, C	0.040
Phosphorous, P	0.020
Sulfur, S	0.015
Boron, B	0.0060

Stainless Steel 660 Mechanical Properties

 

Properties	Metric	Imperial
Tensile strength	1035 MPa	150100 psi
Yield strength (@strain 0.200%)	759 MPa	110000 psi
Elongation at break	25%	25%
Reduction of area	40%	40%
Hardness, Brinell (estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball)	304	304
Hardness, Knoop (estimated from Rockwell C value)	330	330
Hardness, Rockwell C	32	32
Hardness, Vickers (estimated from Rockwell C value)	318	318

Stainless Steel 660 Other Designations

AISI 660	AMS 5525	AMS 5726	AMS 5732	AMS 5734
AMS 5731	AISI 662	AMS 5737	AMS 5804	AMS 5895
AMS 5853	AMS 5805	AMS 5858	DIN 1.4943	SPS M250
DIN 1.4944	GE B50T81	GE B50T12	GE B50T1181	ASTM A453 Grade 660
ASTM A638 Grade 660

Available Sizes And Specifications

660 stainless steel profile sizes and specifications
Grade	660
Specification	EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO
Standard	ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 .
Stainless steel round Bar	Diameter: 2mm - 600mm
Stainless steel bright Bar	Diameter: 2mm - 600mm
Stainless steel hex Bar	Dimension: 6mm - 80mm
Stainless steel square bar	Dimension: 3.0 - 180mm
Stainless steel flat bar	Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm
Stainless steel angle bar	as requirements
Length	Normally 6m, or produce as requirements
Surface	Black, Bright. Peeled and Polished, Solution annealed.
Delivery condition	cold drawn, hot rolled, forged, grinding, centerless grinding
Tolerance	H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements

Detection

Processing

 

Packaging & Shipping

Company Profile

FAQ

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .