LORK is a special stainless steel manufacturer with 20 years of manufacturing experience.
C95510 / AMS 4880 is one of the most popular landing gear bushing materials specified today along with C63000 material. This continuous / centrifugal cast alloy is heat treated and exhibits high mechanical strength which meets the properties of C63000 (AMS 4640). In many cases C95510 (AMS 4880) can be substituted for C63000 with the advantage of this material being available in hollow bar, which provides economic cost savings for you, the customer.
AEROSPACE: Landing Gear Bushings & Bearings, Valve Guides, Stems, Seats
INDUSTRIAL: Corrosion Resistant Parts, Wear Rings, Machine Tool Parts, Piston Guides, Worm Wheels, Hot Mill Gurdes
MARINE: Propeller Hubs, Wear Rings, Hardware, Worm Gears, Shafts, Sleeves
SOLID BAR: 1/2" - 12" diameter
HOLLOW BAR (Continuous Cast): thru 10" diameter
C95510 Alloy Specifications
| Product Type | Temper Type |
| Centrifugal | ASTM B271, SAE J462, J461, AMS 4880 |
| Continuous | ASTM B505, SAE J462, J461, AMS 4880 |
| Ingot | ASTM B30 |
| Precision | ASTM B806 |
| Sand | ASTM B148, B763, SAE J461, J462 |
Chemical Composition
The following table shows the chemical composition of copper UNS C95510.
| Element | Content (%) |
| Cu% | 78.00-min |
| Sn% | 0.20 |
| Zn% | 0.30 |
| Fe% | 2.00-3.50 |
| Ni% | 4.50-5.50 |
| Al% | 9.70-10.90 |
| Mn% | 1.50 |
The physical properties of copper UNS C95510 are outlined in the following table.
| Properties | Metric | Imperial |
| Density | 7.58 g/cm³ | 0.274 lb/in³ |
| Melting point | 1035°C | 1895°F |
The mechanical properties of copper UNS C95510 are tabulated below.
| Properties | Metric | Imperial |
| Tensile strength | 780 MPa | 110000 psi |
| Yield strength | 490 MPa | 68200 psi |
| Elongation at break (in 50 mm, 10% reduction in area) | 15% | 15% |
| Elastic modulus | 117 GPa | 17000 ksi |
| Poisson's ratio | 0.34 | 0.34 |
| Reduction of area (at 316°C/601°F, cold finished) | 9% | 9% |
| Shear modulus | 44.0 GPa | 6380 ksi |
| Fatigue strength (at number of cycles 1.00e+8, reverse bending) | 255 MPa | 37000 psi |
| Hardness, Rockwell B | 94 | 94 |
| Machinability (UNS C36000 (free-cutting brass) = 100) | 30 | 30 |