Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe

Product Details
Customization: Available
After-sales Service: Communicate with Us
Warranty: Communicate with Us
Manufacturer/Factory, Group Corporation
Diamond Member Since 2024

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

  • Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
  • Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
  • Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
  • Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
  • Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
  • Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
Find Similar Products
  • Overview
  • Product Description
  • Detection
  • Processing
  • Packaging & Shipping
  • Company Profile
  • FAQ
Overview

Basic Info.

Type
Seamless
Technique
Cold Rolled, Hot Rolled
Material
Stainless Steel
Key Words
pH15-7mo Tube/Pipe
Thickness
2mm - 100mm
Outside Diameter
4mm - 1219 mm
Length
as Your Requirments
Surface
Black, Bright, Polished, Pickling
Sample
Free-Sample
MOQ
100kgs
Tolerance
H8, H9, H10, H11, H12, K11, K12
Stock
in Stock
Transport Package
Wooden Package
Specification
ph15-7mo
Trademark
LORK
Origin
China
HS Code
7505120000
Production Capacity
50000kg/Month

Product Description

Product Description

 

Introduction

15-7 Mo (UNS S15700) is a semi-austenitic precipitation-hardening stainless steel that provides high strength and hardness, good corrosion resistance, and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops an effective balance of properties by simple heat treatments. For application requiring exceptionally high strength, cold-reduced 15-7 Mo Stainless Steel in Condition CH 900 is particularly useful for applications permitting limited ductility and workability. This alloy is particularly beneficial for a wide range of applications that include retaining rings, springs, diaphragms, aircraft bulkheads, welded and brazed honey comb paneling and other aircraft components requiring high strength at elevated temperatures.

Precipitation Hardening Stainless Steel PH15-7MO Applications

▪ Paneling and springs
▪ Diaphragms
▪ Retaining rings
▪ Welded and brazed honeycomb paneling
▪ Aircraft components bulkheads

Formability
The material in Condition A can be formed comparably to Type 301. It work hardens rapidly and may require intermediate annealing in deep drawing or in forming intricate parts. Springback is similar to that of Type 301. This alloy is extremely hard and strong in Condition C, so fabrication techniques for such material must be used.

Weldability

The precipitation hardening class of stainless steel is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to achieve optimum mechanical properties by considering the best heat-treated conditions in which to weld, and which heat treatments should follow welding. This particular alloy is generally considered to have poorer weldability compared to the most common alloy of this stainless class, 17-4 PH Stainless Steel. A major difference is the high Al content of this alloy, which degrades penetration and enhances weld slag formation during arc welding. Also, the austenite conditioning and precipitation hardening heat treatments are both required after welding to achieve high strength levels. When a weld filler is needed, W P 15-7 Mo or W 17-7 PH is most often specified.

PH15-7MO Chemical Composition

Element Content (%)
Iron, Fe Balance
Chromium, Cr 14 -16
Nickel, Ni 6.50 - 7.75
Molybdenum, Mb 2 - 3
Silicon, Si 1
Manganese, Mn 1
Aluminum, Al 0.75 - 1.50
Carbon, C 0.09
Phosphorus, P 0.040
Sulfur, S 0.040

PH15-7MO Mechanical Properties

Property ConditionA ConditionTH 1050 ConditionRH 950 ConditionC ConditionCH 900
UTS, ksi (MPa)
0.2% YS, ksi (MPa)
Elongation % in 2"
Hardness, Rockwell
130 (896)
55 (372)
35
B88
210 (1448)
200 (1379)
7
C44
240 (1655)225 (1552)
6
C48
220 (1517)190 (1310)
5
C45
265 (1828)
260 (1793)
2
C50

Available Sizes And Specifications

15-7 Mo stainless steel plate sizes and specifications
Grade 15-7 Mo
Stainless steel seamless pipe Outside diameter: 4.0 - 1219mm, Thickness: 0.5 -100mm,Length: 24000mm
Stainless steel welded pipe Outside diameter: 6.0 - 2800mm, Thickness: 0.3 -45mm,Length: 18000mm
Stainless steel capillary pipe Outside diameter: 0.4 - 16.0mm, Thickness: 0.1 -2.0mm,Length: 18000mm
Stainless steel welded sanitary pipe Outside diameter:8.0- 850mm, Thickness: 1.0 -6.0mm
Stainless steel seamless sanitary pipe Outside diameter: 6.0- 219mm, Thickness: 1.0 -6.0mm
Stainless steel square pipe Side Length: 4*4 - 300*300mm, Thickness: 0.25 - 8.0mm, Length: 18000mm
Stainless steel rectangular pipe Side Length: 4*6 - 200*400mm, Thickness: 0.25 - 8.0mm, Length: 18000mm
Stainless steel coil pipe Outside diameter: 0.4 - 16mm, Thickness: 0.1 - 2.11mm
Standard American Standard: ASTM A312, ASME SA269, ASTM A269, ASME SA213, ASTM A213 ASTM A511 ASTM A789, ASTM A790, ASTM A376, ASME SA335, B161, SB163, SB338, SB667/668
Germany Standard: DIN2462.1-1981, DIN17456-85, DIN17458-85·
European Standard: EN10216-5, EN10216-2
Japanese Standard: JIS G3463-2006, JISG3459-2012
Russian Standard: GOST 9941-81
 
 

Detection

Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe

Processing

 

Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
 

Packaging & Shipping

 

Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe
Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe

Company Profile

 

Lork Uns S15700/ ASTM A693 Alloy Steel Tube for High Temperature Aircraft Parts 15-7mo Stainless Steel Pipe

FAQ


Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .