Lork Manufacture Th1050 Stainless Steel Bar for Diaphragms Precipitation Hardening 15-7 Mo Rod

• Type: Stainless Steel Bars
• Standard: ASTM, AISI, GB, JIS, DIN, EN
• Grade: pH15-7mo
• Shape: Round
• Technique: Cold Rolled, Hot Rolled
• Surface Treatment: Pickling
• Model NO.: 15-7mo bar
• Key Words: pH15-7mo Rod Supplier
• Diameter: 2mm - 600mm
• Length: as Your Requirments
• Surface: Black, Bright, Polished, Pickling
• Sample: Free-Sample
• MOQ: 100kgs
• Tolerance: H8, H9, H10, H11, H12, K11, K12
• Stock: in Stock
• Transport Package: Wooden Package
• Specification: ph15-7mo bar
• Trademark: LORK
• Origin: China
• HS Code: 7505120000
• Production Capacity: 50000kg/Month

Product Description

Product Description

Introduction

15-7 Mo (UNS S15700) is a semi-austenitic precipitation-hardening stainless steel that provides high strength and hardness, good corrosion resistance, and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops an effective balance of properties by simple heat treatments. For application requiring exceptionally high strength, cold-reduced 15-7 Mo Stainless Steel in Condition CH 900 is particularly useful for applications permitting limited ductility and workability. This alloy is particularly beneficial for a wide range of applications that include retaining rings, springs, diaphragms, aircraft bulkheads, welded and brazed honey comb paneling and other aircraft components requiring high strength at elevated temperatures.

Precipitation Hardening Stainless Steel PH15-7MO Applications

▪ Paneling and springs
▪ Diaphragms
▪ Retaining rings
▪ Welded and brazed honeycomb paneling
▪ Aircraft components bulkheads

Formability
The material in Condition A can be formed comparably to Type 301. It work hardens rapidly and may require intermediate annealing in deep drawing or in forming intricate parts. Springback is similar to that of Type 301. This alloy is extremely hard and strong in Condition C, so fabrication techniques for such material must be used.

Weldability

The precipitation hardening class of stainless steel is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to achieve optimum mechanical properties by considering the best heat-treated conditions in which to weld, and which heat treatments should follow welding. This particular alloy is generally considered to have poorer weldability compared to the most common alloy of this stainless class, 17-4 PH Stainless Steel. A major difference is the high Al content of this alloy, which degrades penetration and enhances weld slag formation during arc welding. Also, the austenite conditioning and precipitation hardening heat treatments are both required after welding to achieve high strength levels. When a weld filler is needed, W P 15-7 Mo or W 17-7 PH is most often specified.

PH15-7MO Chemical Composition

Element	Content (%)
Iron, Fe	Balance
Chromium, Cr	14 -16
Nickel, Ni	6.50 - 7.75
Molybdenum, Mb	2 - 3
Silicon, Si	1
Manganese, Mn	1
Aluminum, Al	0.75 - 1.50
Carbon, C	0.09
Phosphorus, P	0.040
Sulfur, S	0.040

PH15-7MO Mechanical Properties

Property	ConditionA	ConditionTH 1050	ConditionRH 950	ConditionC	ConditionCH 900
UTS, ksi (MPa) 0.2% YS, ksi (MPa) Elongation % in 2" Hardness, Rockwell	130 (896) 55 (372) 35 B88	210 (1448) 200 (1379) 7 C44	240 (1655)225 (1552) 6 C48	220 (1517)190 (1310) 5 C45	265 (1828) 260 (1793) 2 C50

Available Sizes And Specifications

15-7 Mo stainless steel profile sizes and specifications
Grade	15-7 Mo
Specification	EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO
Standard	ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 .
Stainless steel round Bar	Diameter: 2mm - 600mm
Stainless steel bright Bar	Diameter: 2mm - 600mm
Stainless steel hex Bar	Dimension: 6mm - 80mm
Stainless steel square bar	Dimension: 3.0 - 180mm
Stainless steel flat bar	Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm
Stainless steel angle bar	as requirements
Length	Normally 6m, or produce as requirements
Surface	Black, Bright. Peeled and Polished, Solution annealed.
Delivery condition	cold drawn, hot rolled, forged, grinding, centerless grinding
Tolerance	H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements

 

Detection

Processing

 

 

Packaging & Shipping

 

Company Profile

 

FAQ

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .