LORK exports a wide range of monel 400 tube which performs brilliantly in large temperature and concentration ranges.
Aluminum Alloy 3003 is a widely used medium strength aluminum alloy with manganese as its primary alloying element. It has good formability, and may be suitable for applications that require bending, spinning, drawing, stamping and roll forming.
3003 Aluminum Alloy Applications
Aluminum 3003 is used in the following application areas:
| Element | Content (%) |
| Aluminum, Al | 96.7 - 99.0 |
| Manganese, Mn | 1.0 - 1.5 |
| Iron, Fe | ≤ 0.70 |
| Silicon, Si | ≤ 0.60 |
| Zinc, Zn | ≤ 0.10 |
| Copper, Cu | 0.05 - 0.20 |
| Properties | Metric | Imperial |
| Density | 2.73 g/cc | 0.0986 lb/in³ |
| Melting Point | 643 - 654 °C | 1190 - 1210 °F |
| Properties | Metric | Imperial |
| Hardness, Brinell | 55 | 55 |
| Hardness, Knoop | 70 | 70 |
| Tensile Strength, Ultimate | 200 MPa | 29000 psi |
| Tensile Strength, Yield | 186 MPa | 27000 psi |
| Elongation at Break | 10% | 10% |
| Modulus of Elasticity | 68.9 GPa | 10000 ksi |
| Ultimate Bearing Strength | 296 MPa | 42900 psi |
| Bearing Yield Strength | 262 MPa | 38000 psi |
| Poissons Ratio | 0.33 | 0.33 |
| Fatigue Strength | 68.9 MPa | 10000 psi |
| Machinability | 30% | 30% |
| Shear Modulus | 25.0 GPa | 3630 ksi |
| Shear Strength | 110 MPa | 16000 psi |
| Properties | Metric | Imperial |
| Specific Heat Capacity | 0.893 J/g-°C | 0.213 BTU/lb-°F |
| Thermal Conductivity | 154 W/m-K | 1070 BTU-in/hr-ft²-°F AA |