For professionals dedicated to precision, reliability, and excellence in materials research and engineering, the Udimet 500 Reference Material is an indispensable tool. Expertly crafted to meet the exacting standards of researchers, engineers, and quality control experts, this reference material provides comprehensive insights into the composition and properties of Udimet 500-an exceptional member of the superalloy family, highly esteemed for its aerospace, gas turbine, and industrial applications.
Nickel Alloy Udimet 500 Applications
| Nickel (Ni) | 50-55% |
| Chromium (Cr) | 17-19% |
| Molybdenum (Mo) | 2.8-3.2% |
| Titanium (Ti) | 1.0-1.5% |
| Cobalt (Co) | 15-17% |
| Aluminum (Al) | 3.0-3.7% |
| Iron (Fe) | 4.0-5.5% |
| Tantalum (Ta) | 0.5-1.0% |
Udimet 500 is annealed at 1079°C (1975°F) and then cooled in air rapidly.
Standard cooling methods are used for cold forming Udimet 500. Minimization of galling is possible with the usage of heavy duty lubricants and soft die materials though the die life is limited. Tooling is recommended in the cold working process to allow liberal radii and clearances.
Welding processes recommended for Udimet 500 include gas-tungsten arc welding, gas metal-arc welding and shielded metal-arc welding. The welding surfaces should be free from paint, crayon markings or oil.
Udimet 500 is capable of being forged as it is ductile.
Udimet 500 is treated at three different temperatures to be air-hardened.
Conventional methods can be used to form Udimet 400 with ease as it has good ductility. Usage of heavy-duty lubricants is recommended during the cold forming process of this alloy. After the forming process all traces of the lubricant should be cleaned to prevent embrittlement of this alloy at high temperatures.
Udimet 500 can be machined by conventional machining methods. This alloy contains higher strength, gumminess and work-hardening qualities. Usage of water-based coolants is preferred for milling, turning or grinding. Usage of heavy lubricants is preferred for boring, drilling, broaching or tapping operations. Work-hardening of the alloy before the cutting process and chatter can be minimized by tooling and use of heavy duty machining equipment.
Udimet 500 can be age-hardened when heat treated.
| Udimet 500 available sizes and specifications | |
| Grade | Udimet 500 |
| Nickel plate | Thickness: 0.3mm - 150.0mm Width: 1000mm - 3000mm |
| Nickel strip/ nickel foil | Thickness: 0.02mm - 16.0mm Width: 5mm - 3000mm |
| Nickel coil | Thickness: 0.3mm - 16.0mm Width: 1000mm - 3000mm |
| Nickel pipe | Outside diameter: 6mm - 1219mm Thickness: 0.5mm - 100mm |
| Nickel Capillary Pipe | Outside diameter: 0.5mm - 6.0mm Thickness: 0.05mm - 2.0mm |
| Nickel bar | Diameter: Ф4mm - Ф600mm |
| Nickel wire rod | Diameter:Ф0.01mm - Ф6mm |
Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .
Q2: Can I have free sample before making orders?
){kind=link}