Lork Uns S31600/ISO X5crnimo17-12-2/SUS 316/En 1.4401 Stainless Steel Rod for Furnace Components 316 Stainless Steel Bar

• Customization: Available
• After-sales Service: Communicate with Us
• Warranty: Communicate with Us
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Technique: Cold Drawn
• Surface Treatment: Polished
• Key Words: 316 Bar/Rod
• Thickness: 3mm - 150.0mm
• Width: 1000mm - 3000mm
• Length: as Your Requirments
• Diameter Tolerance: H9, H11, H13, K9, K11, K13 etc
• Sample: Free-Sample
• Surface: Lack, Peeled, Polishing, Bright, Sand Blast, Hl
• MOQ: 100kgs
• Transport Package: Wooden Package
• Specification: AISI 316/UNS S31600/AMS 5648/ASTM A484
• Trademark: LORK
• Origin: China
• HS Code: 7219350000
• Production Capacity: 50000kg/Month

Product Description

Product Description

 

Introduction

LORK is a special stainless steel manufacturer with 20 years of manufacturing experience.
 

316 (UNS S31600) is a chromium-nickel molybdenum austenitic stainless steel developed to provide improved corrosion resistance to 304/304L in moderately corrosive environments. It is often utilized in process streams containing chlorides or halides. The addition of molybdenum improves general corrosion and chloride pitting resistance. It also provides higher creep, stress-to-rupture and tensile strength at elevated temperatures.
 

It is common practice for 316L to be dual certified as 316 and 316L. The low carbon chemistry of 316L combined with an addition of nitrogen enables 316L to meet the mechanical properties of 316.
 

316 resists atmospheric corrosion, as well as, moderately oxidizing and reducing environments. It also resists corrosion in polluted marine atmospheres. The alloy has excellent resistance to intergranular corrosion in the as-welded condition. 316/316L has excellent strength and toughness at cryogenic temperatures.
 

316/316L is non-magnetic in the annealed condition, but can become slightly magnetic as a result of cold working or welding. It can be easily welded and processed by standard shop fabrication practices.

 Stainless Steel 316 Applications

▪ Food preparation equipment, especially in chloride environments
▪ Chemical processing, equipment
▪ Laboratory benches and equipment
▪ Rubber, plastics, pulp & paper machinery
▪ Pollution control equipment
▪ Boat fittings, value and pump trim
▪ Heat exchangers
▪ Pharmaceutical and textile industries
▪ Condensers, evaporators and tanks

Related Grades

▪ ASTM/ASME: UNS S31600 / S31603
▪ EURONORM: X1 CrNiMo 17 12 2 / X3 CrNiMo 17 12 2
▪ AFNOR: Z 6 CND 17-11 / Z 2 CND 17-12
▪ DIN: 1.4401 / 1.4404

Corrosion Resistance

▪ Generally more resistant than 304 in range of atmospheric environments and many corrosive media due to the increased chromium
▪ and molybdenum content.
▪ Subject to pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking above about 122°F (50°C).
▪ Considered resistant to potable water with up to about 1000mg/L chlorides at ambient temperatures, reducing to about 500mg/L at
▪ 140°F (60°C).
▪ Usually regarded as the "marine grade stainless steel" - but is not resistant to warm sea water.

Stainless Steel 316/316LChemical Composition

Weight % (all values are maximum unless a range is otherwise indicated)
 

Element	316	316L
Cr	16-18	16-18
Ni	10-14	10-14
Mo	2.0-3.0	2.0-3.0
C	0.08 max	0.03 max
Mn	2.0 max	2.0 max
P	0.045 max	0.045 max
S	0.03 max	0.03 max
Si	0.75 max	0.75 max
Ni	0.1 max	0.1 max

Stainless Steel 316/316L Mechanical Properties

 

Typical	316	316L
0.2% Offset Yield Strength, ksi	44	30 min
, ksi	85	75 min
Elongation in 2 inches, %	56	40min
Reduction in Area, %	69	-
Hardness, Rockwell B	81	95 max

 

Hot Working
316/316L can be easily welded and processed by standard shop fabrication practices.

Hot Forming

 

Working temperatures of 1700 - 2200°F (927 - 1204°C) are recommended for most hot working processes. For maximum corrosion resistance, the material should be annealed at 1900°F (1038°C) minimum and water quenched or rapidly cooled by other means after hot working.

Cold Forming

 

The alloy is quite ductile and forms easily. Cold working operations will increase the strength and hardness of the alloy and might leave it slightly magnetic.
 

Machining
316/316L is subject to work hardening during deformation and is subject to chip breaking. The best machining results are achieved with slower speeds, heavier feeds, excellent lubrication, sharp tooling and powerful rigid equipment.

Available Sizes And Specifications

316/316L stainless steel profile sizes and specifications
Grade	316/316L
Specification	EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO
Standard	ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 .
Stainless steel round Bar	Diameter: 2mm - 600mm
Stainless steel bright Bar	Diameter: 2mm - 600mm
Stainless steel hex Bar	Dimension: 6mm - 80mm
Stainless steel square bar	Dimension: 3.0 - 180mm
Stainless steel flat bar	Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm
Stainless steel angle bar	as requirements
Length	Normally 6m, or produce as requirements
Surface	Black, Bright. Peeled and Polished, Solution annealed.
Delivery condition	cold drawn, hot rolled, forged, grinding, centerless grinding
Tolerance	H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements

Detection

Processing

 

Packaging & Shipping

Company Profile

FAQ

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .