| Customization: | Available |
|---|---|
| Product Type: | Tube/Pipe |
| Material: | Aluminum Alloy |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
LORK exports a wide range of monel 400 tube which performs brilliantly in large temperature and concentration ranges.
2024 aluminum is heat-treatable aluminum alloy with copper as the primary alloying element. It is malleable when in the fully soft, annealed temper and can be heat-treated to high strength levels after forming. Due to its high strength to weight ratio, it is widely used in aerospace applications.
2024 Aluminum Alloy Applications
UNS A92024,
Al2024-O,
Alclad 2024-O,
AA2024-T3,
Al2024-T3,
Alclad 2024-T3,
UNS A82024,
Alclad 2024-T4/T351,
Al2024-T4,
UNS A82024,
Alclad 2024-T851
ASTM
B209
B211
QQ-A-225/6
QQ-A-250/4
WW-T700/3
AMS
4037
4120
Chemical Composition
The following table shows the chemical composition of Aluminium / Aluminum 7050 alloy.
| Element | Content (%) |
| Aluminum, Al | 89 |
| Copper, Cu | 2.3 |
| Magnesium, Mg | 2.3 |
| Zinc, Zn | 6.2 |
| Zirconium, Zr | 0.12 |
| - O | -T3 | -T351/T4 | -T851 | |
| Density | 0.1 lb/in3 | 0.1 lb/in3 | 0.1 lb/in3 | 0.1 lb/in3 |
| Ultimate Tensile Strength | 27 ksi(bare); 26 ksi(clad) | 70 ksi(bare); 65 ksi (clad) | 67 ksi(T351); 69 ksi(T4) | 75 ksi |
| Yield Tensile Strength | 11 ksi | 50 ksi(bare); 45 ksi(clad) | 47 ksi(T351); 45 ksi(T4) | 66 ksi |
| Fatigue Strength | 13 ksi | 20 ksi | 20 ksi | 17 ksi |
| Shear Strength | 18 ksi | 41 ksi(bare); 40 ksi(clad) | 41 ksi | 43 ksi |
| Shear Modulus | 4,060 ksi | 4,060 ksi | 4,060 ksi | 3,920 ksi |
| Hardness Rockwell | Brinell | N/A | 47 | B75 | 120 | B75 | 120 | B84 | 140 |
| Elongation at Break Percentage | 20% | 18% | 13%(T351); 16%(T4) | 4.9% |
| Modulus of Elasticity | 10,600 ksi | 10,600 ksi | 10,000 ksi | 10,000 ksi |
| Poisson's Ratio | 0.33 | 0.33 | 0.33 | 0.33 |
| Machinability Percentage | 30% | 70% | 70% | 70% |
| Melting Point | 935-1,180 °F | 935-1,180 °F | 930-1,180 °F | 930-1,180 °F |
| Specific Heat | 2.1 x 10^-1 BTU/lb-°F | 2.09 x 10^-1 BTU/lb-°F | 2.1 x 10^-1 BTU/lb-°F | 2.1 x 10^-1 BTU/lb-°F |
| Thermal Conductivity | 1,340 BTU-in/hr-ft^2-°F | 840 BTU-in/hr-ft^2-°F | 840 BTU-in/hr-ft^2-°F | 1,050 BTU-in/hr-ft^2-°F |
| Electrical Conductivity | 30% IACS | 30% IACS | 30% IACS | 30% IACS |
| Properties | Metric | Imperial |
| Hardness, Brinell | 120 | 120 |
| Hardness, Knoop | 150 | 150 |
| Hardness, Rockwell A | 46.8 | 46.8 |
| Hardness, Rockwell B | 75 | 75 |
| Hardness, Vickers | 137 | 137 |
| Ultimate Tensile Strength | 469 MPa | 68000 psi |
| Tensile Yield Strength | 324 MPa | 47000 psi |
| Elongation at Break | 19 % | 19 % |
| Elongation at Break | 20 % | 20 % |
| Modulus of Elasticity | 73.1 GPa | 10600 ksi |
| Ultimate Bearing Strength | 814 MPa | 118000 psi |
| Bearing Yield Strength | 441 MPa | 64000 psi |
| Poisson's Ratio | 0.33 | 0.33 |
| Fatigue Strength | 138 MPa | 20000 psi |
| Shear Modulus | 28 GPa | 4060 ksi |
| Shear Strength | 283 MPa | 41000 psi |