321 (UNS S32100) is a titanium stabilized austenitic stainless steel with good general corrosion resistance. It has excellent resistance to intergranular corrosion after exposure to temperatures in the chromium carbide precipitation range of 800 - 1500°F (427 - 816°C). The alloy resists oxidation to 1500°F (816°C) and has higher creep and stress rupture properties than alloys 304 and 304L. It also possesses good low temperature toughness.
321H (UNS S 32109) is the higher carbon (0.04 - 0.10) version of the alloy. It was developed for enhanced creep resistance and for higher strength at temperatures above 1000oF (537°C). In most instances, the carbon content of the plate enables dual certification.
321 cannot be hardened by heat treatment, only by cold working. It can be easily welded and processed by standard shop fabrication practices.
321 stainless steel plate is also advantageous for high temperature service because of its good mechanical properties. 321 stainless steel plate offers higher creep and stress rupture properties than 304 and, particularly, 304L, which might also be considered for exposures where sensitization and intergranular corrosion are concerns.
Stainless Steel 321 Applications
Weight % (all values are maximum unless a range is otherwise indicated)
Element | 321 | 321H |
Cr | 17-19 | 17-19 |
Ni | 9-12 | 9-12C |
C | 0.08 max | 0.04-0.14 |
Mn | 2.0 max | 2.0 max |
P | 0.045 max | 0.045 max |
S | 0.03 max | 0.03 max |
Si | 0.75 max | 0.75 max |
Ti | 5*(C+N)-0.7 | 4(C+N)-0.7 |
Fe | Balance | Balance |
Typical Values at 68°F (20°C)
Yield Strength | Ultimate Tensile Strength | Elongation | Hardness | ||
Psi(min) | MPa | Psi(min) | MPa | % (min) | (max) |
30,000 | 205 | 75,000 | 515 | 40 | 217 (HB) |
321/321H stainless steel profile sizes and specifications | |
Grade | 321/321H |
Specification | EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO |
Standard | ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 . |
Stainless steel round Bar | Diameter: 2mm - 600mm |
Stainless steel bright Bar | Diameter: 2mm - 600mm |
Stainless steel hex Bar | Dimension: 6mm - 80mm |
Stainless steel square bar | Dimension: 3.0 - 180mm |
Stainless steel flat bar | Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm |
Stainless steel angle bar | as requirements |
Length | Normally 6m, or produce as requirements |
Surface | Black, Bright. Peeled and Polished, Solution annealed. |
Delivery condition | cold drawn, hot rolled, forged, grinding, centerless grinding |
Tolerance | H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients' requirements |