Ti 6Al-4V Pipe offers a combination of high strength, light weight, formability and corrosion resistance which have made it the most commonly used titanium alloy. It is an alpha+beta alloy that is heat treatable to achieve moderate increases in strength and is recommended for use at service temperatures up to approximately 660°F (350°C). Ti 6Al-4V Pipe may be considered in any application where a combination of high strength at low to moderate temperatures, light weight and excellent corrosion resistance are required.
| V | Al | Fe | O | C | N | H | Y | Ti | Remainder Each | Remainder Total | |
| Min | 3.5 | 5.5 | -- | -- | -- | -- | -- | -- | -- | -- | -- |
| Max | 4.5 | 6.75 | .3 | .2 | .08 | .05 | .015 | .005 | Balance | .1 | .3 |
| Grade | UNS | DIN | EN | ASTM | AMS |
| Ti-6Al-4V | UNS R56400 | ASTM F1475 ASTM B265 Grade 5 |
AMS 4928 |
| Density | Young's Modulus | Shear Modulus | Bulk Modulus | Poisson's Ratio | Tensile Yield Stress | Tensile Ultimate Stress | Hardness | Uniform Elongation | |
| Min | 4.429 g/cm3 (0.160 lb/cuin) | 104 GPa (15.1×106 psi) | 40 GPa (5.8×106 psi) | 96.8 GPa (14.0×106 psi) | 0.31 | 880 MPa (128,000 psi) | 900 MPa (130,000 psi) | 36 Rockwell C (Typical) | 5% |
| Max | 4.512 g/cm3 (0.163 lb/cuin) | 113 GPa (16.4×106 psi) | 45 GPa (6.5×106 psi) | 153 GPa (22.2×106 psi) | 0.37 | 920 MPa (133,000 psi) | 950 MPa (138,000 psi) | -- | 18% |